Electrode for electrolytic capacitor and process of producing the same

ABSTRACT

This invention provides an anodic electrode for an electrolytic capacitor having high capacitance with low-resistance properties at high frequencies and is capable of carrying large current, and a process of producing the same. Such an anodic electrode for electrolytic capacitor includes a porous body that have micropores to be formed with dielectric layer therein and to be filled with electrolyte therein, wherein the porous body includes a laminate of a plurality of sinter layers having the micropores formed from valve metal particles. The laminate includes multilaminarly smaller micropore-size regions and larger micropore-size regions to form electric conductive passages between the smaller micropore-size regions and side surfaces of the porous body to reduce resistance of the capacitor and also increase capacitance by utilizing the smaller micropores-size regions for capacitor effectively. The porous body is formed by stacking a plurality of porous preforms such as sheets preformed of valve metal powder into a laminate, and then sintering the laminate. The porous body may be joined with a valve metal substrate during sintering, thereby completing the anodic electrode for an electrolytic capacitor. Particularly, the porous body may be a laminate including large micropore-size sinter layers and small micropore size sinter layers, by alternatively laminating two types of preforms different in its density.

BACKGROUND OF THE INVENTION

[0001] 1. Filed of the Invention

[0002] The present invention relates to an electrode for electrolytic capacitor and a process of producing the same.

[0003] 2. Prior Art

[0004] Electrolytic Capacitors have historically been increased in capacitance—higher and higher capacitance in smaller and smaller packages. Electrolytic capacitors are often used on the secondary side of a smoothing circuit of direct power supply to assist the promptly starting operation of a central processing unit used for computers such as personal computers and, such capacitors are, in particular, required to have excellent high-frequency properties of the discharging of a large current to the units.

[0005] Various improvements have been made in the electrodes, particularly, anodes to be used in such electrolytic capacitors to meet these requirements. For aluminum electrolytic capacitors, in which usually an anode is formed of aluminum foil subjected to surface area-enlarging treatment by etching, it has been proposed to form finer capillaries in the metal foil by stepping up the etching level. The etched anode metals are anodized to form a dielectric layer on micropore surface having increased area in the anode metal foil, thus, the increased surface area of the dielectric layer resulting in an increased capacitance of the capacitor.

[0006] A tantalum capacitor utilizes, as the electrode, a porous body made by sintering fine powder of metal tantalum, which has valve metal function. The porous electrode has micropores in the porous body and can have significantly great specific surface area. By anodizing the metal porous body, the dielectric layer is formed on the inner surface of the micropores, obtaining large surface area. The provision of capacitance on the all surface of the micropores enables the total capacitance of the capacitor to be increased.

[0007] Capacitor electrodes made from fine power of a metal that has valvular function such as tantalum, aluminum and niobium are disclosed in, for example, Japanese Patent Publication No. 63-283012, Japanese Utility Model Publication Nos. 57-138330, 58-187136, and 59-187129. The capacitor electrodes disclosed in these publications are made by planting a lead wire 41 in a sintered porous body 29 as an anode made from fine power of a metal that has valvular action, as shown in FIG. 8. In addition, the publications quoted above have proposed that a portion of the porous body in the porous body at which the lead is embedded should be worked thin and flat, that the embedded portion of the lead is limited to some length, and that the porous body is limited to a certain degree of flatness of the porous body at the portion where the lead 16 is embedded in the sintered body.

[0008] Now a conventional method commonly employed to manufacture a tantalum capacitor will be described below. A block has been compressed from a metal tantalum fine powder having micropores corresponding to a high specific surface area having a grade of about 30000 μF·V/g of equivalent capacitance per unit weight, in specified dimensions and is sintered to a porous body for an anode. Then a dielectric layer has been formed on the porous body in a known manner by anodizing. At this time, the micropores of the porous body formed by the dielectric layers are filled with an electrolyte of, for example, manganese dioxide. Then, the tantalum capacitor has been completed by attaching a cathode-connecting electrode to the porous body in known manner.

[0009] In order to provide a capacitor having higher capacitance, a tantalum capacitor of higher capacitance should have been achieved by sintering a metal tantalum having greater specific surface area of the micropores corresponding to an equivalent capacitance of, for example, 50000 μF·V/g, to form the similar dimensions of a block as those described above.

[0010] Actually, the tantalum capacitor produced using the fine powder of 50000 μF·V/g was not produced so high in capacitance as expected from the equivalent capacitance, and high-frequency characteristic of the capacitor was lowered unsatisfactory, thus resulting in undesirable characteristic for carrying a large current.

[0011] Such insufficient capacitance of the electrolytic capacitor of the prior art is considered to be caused primarily by the insufficient filling of the electrolyte in the micropores of the porous body to be make the anode. That is, the electrolyte that substantially performs the function of the anode does not sufficiently reach the dielectric layers of the micropores, and therefore the micropores are not fully utilized to provide capacitance.

[0012] A second reason is that, since the porous body has not been provided with sufficient surface area of the electrolyte as a cathode disposed on the body surface to be jointed and covered with the cathode-connection electrode of a internal contact layer such as silver-containing conductive resin through a graphite layer in direct contact with the cathode, the contact resistance between the electrolyte and the cathode-connection electrode have been increased. Thus, equivalent series resistance of the total conventional capacitor could not decrease, resulting in poor high-frequency characteristic.

[0013] In order to overcome the above problems, it was necessary to fill the electrolyte into the micropores in the porous body and increase outer surface area of the valve metal porous body to connect with the cathode-connection electrode, then to make the equivalent series resistance lower.

SUMMARY OF THE INVENTION

[0014] An object of the present invention is to provide an anodic electrode for use of an electrolytic capacitor that has a high capacitance and excellent high-frequency characteristic, while being capable of carrying a large current.

[0015] Another object of the present invention is to provide a process of producing said electrode.

[0016] In the anodic electrode for electrolytic capacitor of the present invention, laminated regions of large size micropores are established in a porous body of valve metal in order to make electric current passages to reach fine size micropore regions which can exhibit high capacitance, then, reducing the inner resistance and increasing the capacitance for the electrode.

[0017] Further, in the anodic electrode for electrolytic capacitor of the present invention, side surfaces of the porous body is expanded by linear recesses and/or projections, such as grooves or corrugations, formed on the side surfaces of the porous body, and then, the increased area of the outer surface can reduce the contact resistance between the porous body and a cathode-connecting electrode material attached on the outer surface to be connected to a cathode lead.

[0018] In this description, an anodic electrode for electrolytic capacitor comprises at least a porous body of a valve metal as an anode of a capacitor, and may include a valve metal substrate for an anode electric collector.

[0019] To realize such an anodic electrode for electrolytic capacitor in the present invention, the porous body of valve metal may includes a laminate of a plurality of sinter layers having micropores. In this case, the laminated regions of larger size micropores are formed in the vicinity of the interfaces between the adjacent sinter layers than inside each of the sinter layers. The larger micropore-size regions close to the interfaces, when filled with solid electrolyte, are used for electric current passages to the inner region of the sinter layers then reducing inner resistance.

[0020] Such a laminate in the porous body may be formed by sintering a laminate composed of a plurality of preforms which are previously formed from a powder of valve metal.

[0021] In another aspect of the invention, the larger micropore-size regions and the smaller micropore-size regions may be at least two types of sinter layers different quantitatively in certain properties.

[0022] The larger micropore-size region may the sinter layers having large micropores which are made contact with other sinter layers having smaller micropores. The larger micropore-sized sinter layers and the smaller micropore-sized sinter layers are laminated of preforms having large micropores of a valve metal powder and preforms having small micropores of the same, respectively.

[0023] The laminate may includes a larger micropore-sized sinter layer as a first type of sinter layer and a smaller micropore-sized sinter layer as a second type of sinter layer which are laminated in contact with each other, at least one side of a first type of layers making contact to a side of the other type of sinter layer. The larger micropore-sized sinter layers provided in the porous body may be capable of be filled with solid electrolyte so as to be used for current passages to decrease inner resistance and the smaller micropore size sinter layers which increase the capacitance because of high specific surface area of micropode in the layer, resulting in increasing in total capacitance of the porous body, along with reduction in inner resistance.

[0024] The laminate of the porous body may include sinter layers having different density of the layers. In this anodic electrode, the laminate may include a high density sinter layers and low-density sinter layers which are laminated in contact with a high density sinter layer.

[0025] Furthermore, in the anodic electrode of the present invention, the laminate of the porous body may be formed of sinter layers having a higher specific surface area and sinter layers having a lower specific surface area are laminated.

[0026] In the invention, the porous body preferably may have corrugated surfaces for connection with a cathode-connecting electrode to decrease the contact resistance therewith. For this purpose, a laminate of two types of preforms having different thermal shrinkage ratio during sintering my be used for being sintered into sintered layers in the porous body.

[0027] A process of fabricating such a laminate may comprise sintering a laminate of a plurality of preforms which are prepared from at least two types of preforms having different properties.

[0028] Another process of the present invention, the plurality of preforms may include the first type of preform s and the second type of performs having of preform densities different from each other, and the two types of preforms are laminated and the laminate is sintered, to fabricate the porous body.

[0029] In a process of producing such a porous body, at least two types of preforms, which are made from valve metal powders having different specific surface areas of the micropores per unit weight, is laminated in a laminate, and sintered into a porous body.

[0030] Particularly, the anodic electrode for electrolytic capacitor of the present invention may be produced by sintering a laminate of two types of preforms made from powders of secondary particles having different physical strengths agglomerated from primary particles of a valve metal.

[0031] Further, it is preferable that the preforms are made sufficiently thin in the shape of plate or sheet, and the porous body is joined with a valve metal substrate, or metal foil so that the valve metal foil is disposed substantially in parallel to the sinter layers formed of the preforms. Alternatively, the valve metal substrate may be disposed substantially perpendicular to the sinter layers.

[0032] Further, in the process, the preforms may include plates or sheets formed of valve metal powder. The plates or sheets may be stacked on the substrate of valve metal foil, the laminate being sintered as a whole. In another process, first the porous body may be formed by sintering the laminate of the preforms, and then the sintered porous body is joined, either in parallel or perpendicularly, with the valve metal substrate.

BRIEF DESCRIPTION OF THE DRAWINGS

[0033] The present invention will be described in detail below with comparative to the following drawings, as follows:

[0034]FIG. 1A is a sectional view showing an anodic electrode for electrolytic capacitor according to an embodiment of the present invention;

[0035]FIG. 1B shows the sectional view of the laminate which is stacked with a plurality of thin preforms according to the an embodiment of the present invention;

[0036]FIG. 2A is a sectional view showing the an anodic electrode for electrolytic capacitor having a porous body sintered according to another preferable embodiment of the present invention;

[0037]FIG. 2B is the sectional view of the laminate which is stacked with a plurality of two types of thin preforms according to the an embodiment of the present invention;

[0038]FIG. 2C is a sectional view showing the an anodic electrode for electrolytic capacitor having a porous body according to another embodiment of the present invention;

[0039]FIG. 3 is an schematically enlarged sectional view showing a porous body sintered of a preform laminate according to an embodiment of the present invention;

[0040]FIG. 4 is an schematically enlarged sectional view showing an porous body sintered of a preform laminate of two types of preforms according to an embodiment of the present invention;

[0041]FIG. 5A is a sectional view of a laminate of the thin preform and a metal foil attached to the laminate according to an embodiment of the present invention;

[0042]FIG. 5B is a sectional view of an electrode including a porous body sintered according to an embodiment of the present invention;

[0043]FIG. 6 shows a sectional view of an electrolytic capacitor fabricated from the electrode according to an embodiment of the present invention;

[0044]FIG. 7 shows a sectional view of an electrolytic capacitor, similarly to FIG. 6. according to an embodiment of the present invention; and

[0045]FIG. 8 is a schematic view showing a prior art tantalum pellet for electrolytic capacitor.

PREFERRED EMBODIMENT OF THE INVENTION

[0046] A basic structure of an anodic electrode for electrolytic capacitor of the invention comprises a porous body of valve metal of laminated sinter layers which has a great number of micropores in mutual communication. The laminated sinter layers are formed by sintering a laminate of preforms.

[0047] The preforms may be formed of a powder of valve metal into a desired shape. As a valve metal, tantalum, titanium, niobium etc. may be used for the anodic electrode. The powder may include refined particles of the metal having complicated configuration with very large specific surface area on each particle. Tantalum may preferably be referred to as the example of valve metal, and such a metal powder may be supplied from the potassium reduction process using potassium tantalum fluoride material. The preform may be thin in plate or sheet shape, favorably to be less than 1 mm. The thin preforms may be made by pressing the powder in a press, maintaining a suitable porous state.

[0048] In a process of producing the such an anodic electrode for electrolytic capacitor, a method of fabricating the porous body comprises: forming porous preforms from powders of valve metal; stacking a plurality of the porous preforms into a laminate; and sintering the preform laminate at a sintering temperature to form a porous body.

[0049] As an instance, as shown FIG. 1A, the structure of the electrode 8 includes a porous body 2 having micropores and a valve metal substrate 4, which may be of foil, joined therewith, wherein the porous body 2 is laminated with a plurality of sinter layers 20 corresponding to preforms 10 stacked as shown in FIG. 1B.

[0050] The sintered porous body 2, as shown in FIG. 3, has a larger micropore regions 22 being in lower density in the vicinity of a jointed interface 21 sintered at which two of the preforms 20 are joined with each other, as compared to an inner region of each sinter layer 20. The large size micropores in the larger micropore region 22 on and close to the jointed interface region are easily capable of being filled with solid electrolyte sufficiently in the electrolyte filling step, so that the electrolyte can passes through the relatively large size micropores in the larger micropore region 22 close to the jointed interface 21, thereby allowing the smaller micropores in each sinter layer to be filled sufficiently with the electrolyte. The large micropore regions 22 around the interfaces 21 can function to provide the law resistance current passage and the finer micropores in the each sinter layer 20 provides high capacitance due to its large specific surface area filled with the electrolyte, thus the layered porous body of the electrode of the present invention showing properties of both low inner resistance and high capacitance.

[0051] In the present invention, by sintering the laminate of the plurality of preforms 10 as shown in FIG. 1B, thin paralleled grooves 33 may be formed on the external, side surfaces 3 of the sintered porous body 2, as shown in FIG. 1A, along lines of the joint interfaces 21 occurring due to laminating surfaces 11 of the preforms 10, dependently on such conditions as intering temperatures, sintering time, the nature of the powder and preform density. As a result of the expansion of the side surfaces 3 of the porous body 2 which are to be joint areas jointing with an cathode-connecting electrode, the contact area of a cathode-connecting electrode attaching to the side surface 3 is increased, then allowing the capacitor to reduce in contact resistance at the cathode-connecting electrode, thus high-frequency characteristics being improved in addition of lowered inner resistance due to the presence of larger micropore regions.

[0052] In another embodiment of the invention, it is preferable that two types of the sinter layers having quantitatively different properties may be used to establish the larger micropore regions laminar in the sintered laminate. Such properties may be selected from different micropore sizes in the sinter layers, i.e., the first type of sinter layer 2 a may be set to be large micropore-sized sinter layers (enlarging the larger micropore regions as shown in FIG. 4) and the second type of sinter layer 2 b to be smaller micropore-sized sinter layers, and the larger micropore-sized sinter layers may be readily impregnated with electrolyte to decrease inner resistance between the side surface 3 of porous body 2 and the smaller micropore-size sinter layers 2 a (the second type of the sinter layers 2 b) as shown in FIGS. 2A, 2C and 4. The smaller micropore-sized sinter layers have high capacitance density and are sufficiently filled with the electrolyte through the larger pored-sinter layers, then increasing the capacitance due to high specific surface in the smaller micropore-sized sinter layers.

[0053] As example of micropore sizes, the smaller micropore size sinter layers may have 0.05 to 0.3 μm and the larger micropore size sinter layer may have 0.3 to 1.5 μm represented by peak value of pore size distribution in a layer. The pore size are expressed by the peak value of the measured micropore size distribution by the traditional mercury microporosimeter technique and the ratio of the peak values of micropore sizes of the smaller micropore size sinter layer to the larger micropore size sinter layer may preferably be set to be in a range of 1.2 to 5.0.

[0054] The laminate of the porous body may be formed of low-density sinter layers as first type of sinter layer 2 a and high-density sinter layers as second type of sinter layer 2 b, wherein the low-density sinter layers function as the larger pore size sinter layer, as mentioned above, which are sufficient filled electrolyte to be used for current passages to decrease inner resistance, and the high-density sinter layers function as the smaller micropore-size sinter layer which increase the capacitance. Further, the high-density sinter layers and the low-density sinter layers are laminated one on another alternately to form the laminate.

[0055] The first type and the second type of sinter layer may have 1.1 to 3.0 of a sinter layer density ratio. The high density sinter layers may preferably be in range of 5.5 to 7.5 g/cm³ and the low density sinter layers may be in the range of 2.5 to 5.5 g/cm³, which exhibit larger micropore size in the layers for the low resistance passages.

[0056] The porous body made of such a laminate comprising two types of sinter layers may preferably have corrugated surfaces, having linear recesses 31 and/or projections 32 on the side surfaces 3 of the porous body to be attached a cathode-connecting electrode, as shown in FIGS. 2A and 4.

[0057] In an anodic electrode for electrolytic capacitor in the invention, the porous body may be made by sintering the stack of two types of preforms 1 a and 1 b having different qualities such as densities, i.e., lower density preforms as the first type of preform 1 a with micropores of larger pore size, and higher density preforms as the second type of preform 1 b with micropores of smaller size. Thus, the micropores in the sinter layers 2 a of lower density can be sufficiently filled with the electrolyte.

[0058] Also, the sinter layer of lower density (from first type of preform 1 a) experiences smaller amount of shrinkage than the sinter layer of higher density (from second type of preform 1 b) after sintering at low sintering temperatures, resulting in corrugation of the external surface, i.e., liner recesses 31 due to the low density-sinter layers (the first type of the sinter layer 2 a) and linear projections 32 due to the high density-sinter layers (second type of layers 2 b) on the side surface 3 in a direction of the joint interfaces 21 layered in the porous body 2 as shown in FIG. 4. Surface area of the side surfaces 3 of the porous body 2 may be increased 1.2 to 1.6 times as much as flat area of the side surface without any surface corrugation, thereby to decrease the contact resistance between the side surface and the cathode-connecting electrode.

[0059] Part of the sinter layers may have lower specific surface area of micropores as the first type of sinter layer, functioning as larger pore-sized sinter layers having the electric current passages for reducing the inner resistance. Thus, the second type sinter layers having the higher specific surface area have function of increasing capacitance. In order to fabricate this anodic electrode, a laminate of at least two types of preforms having different specific surface areas of micropores per unit weight is used with preforms being stacked alternately and sintered. The first type of preform 2 a having smaller specific surface area of the micropores, which have larger particles of valve metal, can be less easily sintered at low sintering temperatures than the second type of preform 2 b of larger specific surface area of the micropores as discussed above, and then thermal shrinkage ratio of the first of preform to the second type during sintering is smaller accompanied by micropores of larger size, and therefore the first type of preform 2 a can be projected as a line on the side surfaces after sintering, resulting in corrugation of the outer surface of the porous body.

[0060] Thus, the porous body for the anode electrode may comprises a laminate by laminating two type of the sinter layers which are sintered from two types of preforms of valve metals that have a different thermal shrinkage ratio during sintering the preforms. The two type of preform may be pressed from valve metal particles different in particle size, being stacked alternately on one another, and then sintered to be incorporated.

[0061] The laminate sintered from the sinter layers 20 may be joined with the valve metal substrate 4 for an anode electric collector, and the sinter layers 20 may preferably be parallel to the valve metal substrate 4, as shown in FIGS. 1A and 2A and 2C, i.e., the substrate 4 for the anode collector is attached to the stacking surface 34 of the porous body 3. Alternatively, the sinter layers 20 of the laminate may be perpendicular to the valve metal substrate 4 as shown in FIGS. 5A and 5B, i.e., the substrate 4 is attached to one of the side surfaces 3 of the porous body. In these cases, foil, sheet, or plate of valve metal is used as a valve metal substrate 4. Preferably, the valve metal for the substrate may be tantalum.

[0062] In addition, the side surfaces 3 of the porous body 2 comprising two types of the sinter layers may be flat with some narrow grooves as shown in FIG. 2C, similarly to FIG. 1A, without having any such deep corrugation above as shown in FIG. 2A. Such phenomena may occur in the case of substantially equal shrinkage between the first type and second type of sinter layers during the sintering of the corresponding types of preforms in lamination while the grooves are formed along the joint interfaces between the adjacent sinter layers.

[0063] A process of producing an anodic electrode for electrolytic capacitor in the present invention, the porous body being joined to a valve metal foil, which comprises: forming a plurality of porous preforms from powder of valve metal; laminating the plurality of preforms to form a laminate; and sintering the laminate to sinter layers incorporated in the sintered laminate to make the porous body. The resulting porous body is composed of plurality of sinter layers made from by sintering the stacked preforms and has micropores in each sinter layers which is to be formed with dielectric layer in the micropores that are then filled with an electrolyte.

[0064] In this process, the preforms may preferably be prepared by forming powder of the valve metal to a sheet or plate form. For the powder material, tantalum powder, e.g., a powder having high specific surface area which is made by means of potassium reduction of sodium tantalum fluoride may be used. Sheets or plates as preforms preferably may be produced by compressing the powder in a press into thin compacts having suitable density and thickness of the preforms, for example, of 1 mm or less, particularly, less than 0.5 mm or, particularly, 0.5 mm to 0.05 mm.

[0065] For another kind of preforms a method may be adopted to produce from slurried or binderized sheet containing a valve metal powder such as tantalum powder.

[0066] In laminating, the suitable number of preforms are sacked in a laminate to provide a desirable capacitance to a fabricated capacitor. The preforms may be laminated on a substrate of valve metal which may typically be used for an anode electric collector. The multilaminated preforms 10 may be parallel (as shown in FIGS. 1B and 2B) or perpendicular (as shown in FIG. 5A) to the substrate 4 surface and after sintering the porous body 2 is joined with the valve metal substrate 4.

[0067] In sintering, the laminated preforms are fired at sintering temperatures of the valve metal, in a vacuum furnace to sinter each preforms, then producing a porous body comprising sinter layers from the thin preforms. The sintering is accomplished at sintering temperatures suitable for the valve metal, for example, 900 to 1600° C. for tantalum, at which valve metal particles in the preforms are connected with one another leaving a great number of micropores in them, and the preforms are connected with each other into corresponding sinter layers. The sintering temperature may be changed to modify the shrinkage ratio of the preform during sintering, as will be explained.

[0068] By the sintering of the preforms, the sintered laminate in the porous body is formed with a smaller micropore-size region within each of the sinter layer and larger micropore-size regions between the two adjacent sinter layers where the sintering action has been slightly insufficient to connect the adjacent preforms with each other during sintering, and the large micropore region and small micropore region are alternatively repeated to be made laminar. As discussed above, in the present invention, the larger micropore-size regions are useful to form electric conductive passages between the smaller micropore-size regions and side surfaces of the porous body.

[0069] The porous body produced by this process is provided on the side surfaces with a plurality of linear recesses 31 and/or projections 32 parallel to each other which are formed along a direction of the sinter layers on the surface. The linear recesses may be linear grooves 33 along the opening edges of each of the preforms 10 on the side surface 3 during sintering. Such grooves 33 on the side surfaces 3 of the porous body are useful to increase an contact area of the side surfaces 3 which is to be covered with and in contact to a cathode-connecting electrode 5.

[0070] Particularly, in the process, it is desired that the plurality of preforms are composed of at least two types of preforms different quantitatively in properties including density and/or shrinkage, to form large micropore regions more wider, and also to corrugate the side surfaces of the porous body more deeply.

[0071] First, the property of preforms of the two types may include a different thermal shrinkage ratio during sintering. In this case, a first type of preform may show large thermal shrinkage ratio and the second type of preform may have small thermal shrinkage ratio which are stacked in contact each other to form the preform laminate, and thereby the sintered laminate can have side surfaces provided with recesses which have been shrunk relatively deeper corresponding to the first type of preform and with projections which have been shrunk relatively shallower to the second type of the preforms dependently on shrinkage difference between adjacent preforms of the two types under consideration during sintering.

[0072] Further, the process may utilize the plurality of preforms including low density performs as a first type of preform and high density preforms as the second type of preform, which, in laminating, are stacked in contact to each other to form the laminate. The densities imparted to performs can be achieved by controlling the compressing pressures to be added to the powders in forming preforms. The ratio of the high density to the low density in the two types of preforms are set to be in a range of 1.1:1 to 3.0:1. After sintering at relatively low temperatures, low density preforms are changed to low density sinter layers having larger micropores size, as compared with high density sinter layers having smaller-size sinter layers from the second type of preform. The sintering at low temperatures allows the density ratios of the preforms to be maintained in a sinter layers corresponding to each of the two types of preforms.

[0073] Thus, the sinter layers in the porous body to be divided in two parts of high density regions and low density regions in a multilaminar state. The high density sinter layers may preferably be in range of 5.5 to 7.5 g/cm³ and the low density sinter layers may be in the range of 2.5 to 5.5 g/cm³ which the low density sinter layers exhibit larger micropore size in the layers for the low resistance passages.

[0074] As discussed above, the first type of preform 1 a having low density are apt to experiences smaller amount of shrinkage than the second type of preform 1 b (the sinter layer of higher density) during sintering at low sintering temperatures and results in deep corrugation of the side surfaces, comprising liner recesses due to the low density-sinter layers 2 a and projections due to the high density-sinter layers 2 b on the side surface 3 in a direction of the joint interfaces 21 layered in the porous body 2 as shown in FIG. 4. the deep corrugation, thereby, can decrease the contact resistance between the side surfaces 3 and the cathode-connecting electrode 5 in contact to each other as shown in FIGS. 6 and 7.

[0075] However, it is noted that, when sintering carried out at a higher sintering temperature, the projecting and recesses have adverse relation with respect to the high density- and low density-sinter layers with same effects as described above. Higher sintering temperatures can promote the sintering of preforms to density the low density-preforms to ultimate density of solid sintered material, then, the low density-preforms showing greater amount of sinter shrinkage than the high density preforms.

[0076] In anther embodiment of the process, a plurality of preforms comprise at least two types of preforms different in specific surface areas of micropores per unit weight, and in laminating the first type of performs having low specific surface area and the preforms having high specific surface are stacked one on another to form the laminate.

[0077] In this case, for the preforms may be made from two powders different in specific surface areas per unit weight. A powder of tantalum having low specific surface area of micropores per unit weight and the other powder having high specific surface area are pressed to the first and the second types, respectively, of preforms which are laminated alternatively and sintered to a sintered laminate of a porous body. After sintering, the preforms of low specific surface area are changed into larger micropore-size sinter layers to be used for low electric resistance passages between the smaller micropore-size sinter layers to exhibit high capacitance because of effective utilization of the total high micropore areas existing in the smaller micropore-size sinter layers.

[0078] In another process, at least two types of preforms including the first preform and the second preform made from powders of valve metals that have different physical strength of powder, and the first perform and the second preform are stacked one on another to form the laminate.

[0079] Particularly, the anodic electrode for electrolytic capacitor of the present invention may be produced by sintering a laminate of two types of preforms made from powders containing the secondary particles having different physical strengths which are agglomerated from primary particles of a valve metal, and the different types of the preforms are laminated one on another alternatively.

[0080] When a first type of preform 1 a is selected from the powder of secondary particles having higher physical strength, which are coagulated primary particles more strongly by heat treatment, are less capable of being sintered than the powder of lower physical strength of the second type of preform 1 b, then, the thermal shrinkage ratio of the first type of preform 1 a is less than the second type of preform 1 b while accompanied by micropores of larger size and produces linear projections 32 on the side surfaces in the porous body. Sinter layers 2 a having larger micropores in the porous body is more easily filled with electrolyte and improves the efficiency of achieving capacitance. As a result, the equivalent series resistance can be reduced by utilizing the inner regions including larger micropores in the porous body and the region of expanded side surface of the porous body in connection with a cathode-connecting electrode.

[0081] The porous body so produced for an electrode for electrolytic capacitance is anodized in an acid solution such as phosphoric acid to form a dielectric layer in the sinter layers of the porous body and the substrate for an anode electric collector. Thereafter, the porous body is impregnated with a solid electrolyte, preferably such as manganese dioxide. In this case, the anodizes porous body is inserted in a solution of manganese nitrate in water, and then dried and calcined in an oxidizing atmosphere to dissolve the nitrate into manganese dioxide in the micropores. This operation is repeated several times till the oxide is filled almost completely in the micropores in the sinter layers.

[0082] The porous body filled with electrolyte is covered with the out side of the porous body, as shown in FIGS. 6 and 7, with first a graphite layer 51 applied on the porous body 2 and the silver-containing curable paste 50 applied to the graphite layer 51 those comprises a cathode connecting electrode 5, and thereafter, the silver-pasted porous body is housed in a metallic conductive can (not shown) but the anode-electric collector remains exposed outside the can, to obtain a solid electrolytic capacitor 9.

EXAMPLE 1

[0083] First, a number of sheet-like preforms are made by pressing fine powder of a valve metal. Then a valve metal foil is ground to make its surface roughened as a substrate 4 for anode collector. The preforms 1 are stacked on the substrate 4 for an anode electric collector to form a laminate 80. Thereafter, the laminate is sintered to form a porous body 2, thereby completing an electrode 8 for electrolytic capacitor shown in FIG. 1.

[0084] In this example, the porous body 2 is constructed by multilaminated thin sinter layers 1 and the sinter layers 20 are formed by sintering the stacked preforms above, with one preform that is sintered corresponding to one sinter layer 1.

[0085] In the porous body 2 sintered, the large micropores regions, in FIGS. 1B and 3, are formed in the vicinity of a joint interface 21 between sinter layers 20 in contact with each other, and are lower in density than the inner regions of the sinter layers 20 and also larger in micropore size larger than inside the sinter layers 20.

[0086] Moreover, since edges of each preform 10 is rounded during sintering, as shown in FIGS. 1B and 3, a narrow grooves 33 is formed in the vicinity of the joint interface 21 between two sinter layers on the side surface 3 of the porous body 2.

[0087] A portion interposed between adjacent sinter layers 20 of the porous body 2 made by sintering the laminate formed from a number of preforms 10, namely the large micropore regions 22 at the jointed interfaces 21 has a low density, and the micropores formed in this region have larger sizes. In the large micropore regions of lower density, substantial shrinkage occurs after sintering and the shrinkage causes narrow grooves 33 to be formed in the vicinity of the joint interface 21 on the side face of the porous body 2.

[0088] In Example 1, electrolytic capacitors are fabricated as follows. A refined powder of metal tantalum in a grade of 70000 μF·V/g as a measure of specific surface area was pressed into preforms each measuring 1.0 mm×3.0 mm in size and 0.44 mm in thickness, with ten preforms stacked on a tantalum foil as substrate for anode electric collector and sintered at 1350° C. in high vacuum, thereby making an electrode 8 for electrolytic capacitor.

[0089] Then, the electrode 8 for electrolytic capacitor was anodized in phosphoric acid solution maintained at a temperature of about 85° C. with a voltage of 20V applied to formed a dielectric layer in the sinter layers 20 of the porous body, and manganese dioxide was formed as an electrolyte in the porous body by repeated treatments of dipping it in manganese nitrate solution and calcining to manganese oxide. Further, after providing a cathode-connecting electrode 5 consisting of a graphite layer 51 and a conductive resin paste 50 rich in silver particles, an external anode lead and an external cathode lead were connected to the electrode which is molded in a molding resin to complete an electrolytic capacitor. Theoretical capacitance of the electrolytic capacitor made in this process is to be 350 μF.

[0090] As a comparative example, a porous body was made by pressing metal tantalum fine powder into a single large preform measuring 1.0 mm×3.0 mm in size and 4.4 mm in thickness was joined with a valve metal foil made roughened the surface thereof by grinding, with this assembly being sintered to make an anodic electrode for electrolytic capacitor. This capacitor electrode will be hereinafter called the comparative electrode. The density of the porous body of the comparative electrode could be substantially equal to that of the porous body of the anodic electrode for electrolytic capacitor.

[0091] A comparative electrolytic capacitor also was to have theoretical capacitance of 350 μF, which was made from the comparative electrode in a process similar to the process of making the capacitor in a similar manner of Example 1.

[0092] Capacitance was measured at a voltage of frequency of 120 Hz applied thereto and at a voltage at a frequency of 100 kHz applied, and equivalent series resistance at a voltage of resonance frequency of 1 MHz applied was measured. The measure results are set forth in Table 1. TABLE 1 Capacitance Capacitance at 120 Hz at 100 kHz Equivalent series (μF) (μF) resistance (mΩ) Present 322 110 45 invention Comparative 305  83 50 Example

[0093] As is clear from Table 1, the measured capacitance of the capacitor in this example is near the theoretical capacitance and higher than that of the comparative capacitor. The capacitor of this example shows less decrease in capacitance caused by high frequency voltage, as compared with the comparative capacitor. It is also seen that the capacitor of Example 1 has low equivalent series resistance, having excellent high-frequency characteristic and is capable of carrying large ripple current.

[0094] The reason for the capacitor of this example, having such a large capacitance is that larger pores are formed in the jointed interface region in the porous body 2 with the dielectric layer formed in the large pores so that almost all the pores existing in the porous body are capable of being used for capacitor.

[0095] Also, It is seen that the capacitor in the example has excellent high-frequency characteristic because the grooves are formed on the surface of the porous body leading to an increase in the surface area of the porous body, thereby reducing the equivalent series resistance of the capacitor of the first embodiment.

EXAMPLE 2

[0096] In an example of this embodiment, a refined tantalum powder having 70000 μF·V/g of measure of specific surface area per unit weight was used to be pressed into pieces of preforms in a sheet shape of each measuring 1.0 mm×3.0 mm×0.44 mm. Five pieces of a first type of preform with density of 6.0 mg/cm³ and five pieces of the second type of preform 2 b with density of 4.4 mg/cm³ were prepared by altering the pressing draft. The first type and second type of preform 2 a and 2 b are stacked alternately one on another to form a ten-layered laminate on the tantalum foil as a substrate for anode electric collector. This laminate was sintered to make a porous body, thus completing an anodic electrode for electrolytic capacitor of this example. The conditions of sintering the laminate were set similar to those of the first embodiment above.

[0097] An electrolytic capacitor having theoretical capacitance of 370 μF is made from the anodic electrode for electrolytic capacitor 9 similarly to the first example.

[0098] For the comparative example, tantalum fine powder is pressed into a small block measuring 1.0 mm×3.0 mm in size and 4.4 mm in thickness with density of 5.2 mg/cm³, which is sintered to make a porous body. This porous body is joined with a tantalum foil for anode electric collector. Sintering conditions are similar to sintering the porous body of this example.

[0099] A comparative electrolytic capacitor is also to have theoretical capacitance of 370 μF and is fabricated from the above comparative electrode in similar manner to the process of making the capacitor of this example.

[0100] Table 2 shows resulting capacitance data of the capacitors of this example and the comparative which are evaluated under a voltage at frequencies of 120 Hz and 100 kHz applied thereto, and equivalent series resistance under a voltage of resonance frequency 1 MHz is also evaluated. TABLE 2 Capacitance Capacitance at 120 Hz at 100 kHz Equivalent series (μF) (μF) resistance (mΩ) Present 341 139 40 invention Comparative 318  86 55 Example

[0101] As is clear from Table 2, the capacitor in the second example is larger in capacitance than the comparative capacitor and is near the theoretical capacitance. Also the capacitor of this example experiences less decrease in the capacitance that is caused by a voltage of high frequency applied, than the comparative capacitor. It is also shown that the capacitor of this example has the equivalent series resistance, thus exhibiting high-frequency characteristic with capability of carrying large ripple current.

[0102] The reason for the capacitor of the second example having a large capacitance is that the micropores of larger size are formed in the second sinter layer of the porous body of the anodic electrode for electrolytic capacitor. As the large pores are filled with the electrolyte, the pores provide capacitance efficiently.

[0103] Also the capacitor of the second example has lower equivalent series resistance because the side face of the first sinter layer becomes concave resulting in an increase in the surface area of the porous body. The reduction in the equivalent series resistance means a improvement of high-frequency characteristic of the capacitor, in the second example. Adhesive strength of the porous body to the cathode-connecting electrode can also be increased due to the recesses and projections on the side surfaces, thereby improving the reliability of delamination resistance between them.

[0104] The anodic electrode for electrolytic capacitor in these examples are produced from the porous body made by forming the laminate on a metal foil substrate and then sintering the laminate, but the present invention is not limited to this procedure. Alternatively, the anodic electrode for electrolytic capacitor may be produced by first sintering the laminate to form the porous body, then joining the porous body to the metal foil for electrode.

[0105] In the examples described above, preforms of different densities are formed from the same tantalum powder, and are sintered to form the porous body having local differences in the density, the pore size and the thermal shrinkage ratio, but the present invention is not limited to the above conditions. For example, the porous body may also be produced by sintering a laminate formed from a plurality of preforms that are different in the density or the thermal shrinkage ratio which are made by regulating the degree of coagulation of the primary particles or the secondary particles of the tantalum powder and controlling the tantalum powder particle size or bulk density thereof. The preforms may also be made from powders of two or more types of valve metal having different densities or thermal shrinkage ratios. Green sheets may also be used as the preforms.

[0106] As described above, the anodic electrode for electrolytic capacitor of the present invention has the porous body formed by stacking a plurality of preforms to make the laminate and sintering the laminate. The porous body has regions of low density and regions of high density, with micropores of larger size being formed in the regions of low density. When the electrolytic capacitor is made using this electrode, since the larger pores can be sufficiently filled with the electrolyte, an electrolytic capacitor of large capacitance can be obtained. Since the region of higher density has a high thermal shrinkage ratio, grooves are formed on the porous body. Since this increases the surface area of the porous body, connecting resistance with the cathode-connecting electrode is reduced and equivalent series resistance of the electrolytic capacitor decreases, thus improving the high-frequency characteristic. 

1. An anodic electrode for an electrolytic capacitor comprising a porous body that have micropores to be formed with dielectric layer therein and to be filled with electrolyte therein, wherein the porous body comprises a laminate of a plurality of sinter layers having the micropores which are sintered from valve metal particles.
 2. The anodic electrode according to claim 1, wherein the laminate comprises multilaminarly smaller micropore-size regions and larger micropore-size regions to form electric conductive passages between the smaller micropore-size regions and side surfaces of the porous body.
 3. The anodic electrode according to claim 2, wherein the large micropore-size regions are the vicinities of the interfaces between the sinter layers in the laminate, and the small micropore regions are inside the sinter layers.
 4. The anodic electrode according to claim 2, wherein in the laminate the sinter layers comprise two types of sinter layers different quantitatively in properties.
 5. The anodic electrode according to claim 4, wherein the first type of sinter layer comprises larger micropore-sized sinter layers and the second type of sinter layer comprises smaller micropore-sized sinter layers and the sinter layers each both types are laminated in contact with each other.
 6. The anodic electrode according to claim 5, wherein in the laminate the first type of sinter layer comprises low-density sinter layers and the second type of sinter layer comprises high-density sinter layers.
 7. The anodic electrode according to 5, wherein in the laminate the first type of sinter layer has low specific surface area and the second type of sinter layer has low specific surface area.
 8. The anodic electrode according to claim 2, wherein the valve metal is tantalum.
 9. The anodic electrode according to claim 2, wherein the porous body is joined with the valve metal substrate for anode electric collector, and the sinter layers are parallel to the valve metal substrate.
 10. The anodic electrode according to claim 2, wherein the porous body is joined with the valve metal substrate for anode electric collector, and the sinter layers are perpendicular to the valve metal substrate.
 11. The anodic electrode according to claim 2, wherein the porous body is filled with electrolyte impregnated in the micropores.
 12. The anodic electrode according to claim 2, wherein the electrolyte is manganese dioxide.
 13. The anodic electrode according to claim 2, wherein the porous body is covered with and in contact to a cathode-connecting electrode comprising silver-containing paste through a graphite layer therebetween.
 14. The anodic electrode for electrolytic capacitor according to any one of claim 2, wherein the porous body is provided on the side surfaces with a plurality of linear recesses and/or projections parallel to each other which are formed along a direction of the sinter layers on the surface, to increase an contact area of the side surfaces which is to be covered with and in contact to a cathode-connecting electrode.
 15. The anodic electrode according to claim 14, wherein the linear recesses and/or projections parallel is narrow grooves formed along the interface between the sinter layers.
 16. The anodic electrode according to claim 14, wherein in the laminate the sinter layers comprise two types of sinter layers different quantitatively in properties.
 17. The anodic electrode according to claim 14, wherein the sinter layers in the laminate comprise two types of sinter layers different quantitatively in properties, and the linear recesses and/or projections are formed repeatedly along each of the different types of sinter layers on the side surfaces of the porous body.
 18. The anodic electrode according to claim 16, wherein the first type of sinter layer comprises larger micropore-sized sinter layers and the second type of sinter layer comprises smaller micropore-sized sinter layers and the sinter layers each both types are laminated in contact with each other.
 19. The anodic electrode according to claim 18, wherein in the laminate the first type of sinter layer comprises low-density sinter layers and the second type of sinter layer comprises high-density sinter layers.
 20. The anodic electrode according to 18, wherein in the laminate the first type of sinter layer has low specific surface area and the second type of sinter layer has low specific surface area.
 21. The anodic electrode according to any of claims 14 to 10, wherein the valve metal is tantalum.
 22. The anodic electrode according to claim 14, wherein the porous body is joined with the valve metal substrate for anode electric collector, and the sinter layers are parallel to the valve metal substrate.
 23. The anodic electrode according to claim 14, wherein the porous body is joined with the valve metal substrate for anode electric collector, and the sinter layers are perpendicular to the valve metal substrate.
 24. The anodic electrode according to claim 14, wherein the porous body is filled with electrolyte impregnated in the micropores.
 25. The anodic electrode according to 14, wherein the electrolyte is manganese dioxide.
 26. The anodic electrode according to claim 14, wherein the porous body is covered with and in contact to a cathode-connecting electrode comprising silver-containing paste through a graphite layer therebetween.
 27. A process of producing an anodic electrode for electrolytic capacitor, comprising a porous body having micropores which is to be formed with dielectric layer in the micropores that are then filled with an electrolyte, the porous body being joined to a valve metal substrate, wherein the process comprises: forming a plurality of porous preforms from a powder of valve metal; laminating the plurality of porous preforms to form a laminate; and sintering the laminate to sinter layers incorporated in the sintered laminate to make the porous body.
 28. The process according to claim 27, wherein the sintered laminate has multilaminarly smaller micropore-size regions and larger micropore-size regions to form electric conductive passages between the smaller micropore-size regions and side surfaces of the porous body.
 29. The process according to claim 27, wherein the porous body is provided on the side surfaces with a plurality of linear recesses and/or projections parallel to each other which are formed along a direction of the sinter layers on the surface, to increase an contact area of the side surfaces which is to be covered with and in contact to a cathode-connecting electrode.
 30. The process according to any one of claim 29, wherein the plurality of preforms comprise at least two types of preforms different quantitatively in properties.
 31. The process according to any one of claims 30, wherein in laminating the first type of preform having large thermal shrinkage ratio and the second type of preform having small thermal shrinkage ratio are stacked in contact each other to form the laminate, and thereby the sintered laminate is provided with recesses corresponding to the first type of preform and with projections to the second type of the preforms by means of shrinkage difference of the preforms during sintering.
 32. The process according to claim 30, wherein said plurality of preforms comprise the first types of low density performs and the second type of preform having high density preforms which in laminating are stacked in contact to each other to form the laminate.
 33. The process according to claim 30, wherein the plurality of preforms comprise at least two types of preforms different in specific surface areas of micropores per unit weight, and in laminating the first type of performs having low specific surface area and the preform having high specific surface are stacked one on another to form the laminate.
 34. The process according to claim 30, wherein the at least two types of preforms including the first preform and the second preform made from powders of valve metals that have different physical strength of the powder, and the first perform and the second preform are stacked one on another to form the laminate.
 35. The process according to claim 27, wherein the preforms are made in sheet shape by pressing valve metal powder.
 36. The process according to claim 35, wherein in laminating, the sheet-like preforms are stacked on a valve metal substrate for an anode electric collector to form a laminate.
 37. The process according to any one of claim 36, wherein in laminating, the sheet-like preforms of the laminate are disposed substantially in parallel to a valve metal substrate, and in sintering, the porous body is joined with the valve metal substrate.
 38. The process according to claim 36, wherein in laminating, the sheet-like preforms of the laminate are disposed substantially perpendicularly to a valve metal substrate, and in sintering, the porous body is joined with the valve metal substrate. 